Flex is an often overlooked aspect when talking about surfboards, and it plays a huge role in the performance of your surfboard.When people do talk about “flex”, they are usually talking about fins and fin design. We have mentioned the importance of flex in your fins before. Here, however, we will discuss the flex in your surfboard.

 

What is surfboard flex?

Flex in a surfboard has similar principles as the flex in fins: Flex = projection, which means your speed when coming off the bottom, or helping to lay into a nice speed turn off the top.

 

This projection comes from your board bending, or flexing, into the shape of the wave with the force you put down on it, and how it snaps back into shape. It stores up all of that energy and releases it, projecting you forward.

 

Look at it this way. When you drop into the wave and come to your bottom turn, your board will bend slightly to fit the shape of the wave when you power down onto it. This causes a build up energy in the board as it is bending out of its natural shape. Now, when you start to drive up the face and your weight begins to lift, your board recoils back to its original shape, releasing all that pent up energy and projecting you through your turn.

 

The better you become at surfing, the more you can feel this flex and use it to link your maneuvers while constantly generating speed down the line. The trick, for shapers, is knowing how to manipulate this to get the ideal flex properties they are looking for.

 

How do we control flex?

Since polyurethane foam blanks became the norm in surfboard construction, wooden strips call stringers needed to be used down the center of the board. This helped increase the strength of the board and stiffen it up.

 

This was especially handy in longboards, since they tend to flex or bend quite a bit more due to their length. Surfboard shapers soon figured out that the strength and flexibility of the board could be controlled by using stringers of various thicknesses. And sometimes multiple stringers would be used for the same effect, with the added bonus of looking aesthetically pleasing.

 

As shapers and surfers started paying closer attention to the flex and projection of a surfboard, the stringer placement and materials available started becoming more crucial. Still the most common placement for a stringer is down the center of a board. This is more or less the status quo for boards around the world.

 

A board with the center stringer will feel nice and strong under foot which is important. Much of the force put down on your board will be from your feet down the center of the board. This stringer placement however, leaves the rails to be much softer which can result in them flexing, twisting and wobbling differently. This is called torsional flex and can result in slowing your board down a bit.

 

By placing the stringer out towards the rail, you can stiffen the rail line up and give it more spring along its perimeter where the board is in contact with the water when going through turns. Parabolic stringers are often used in this case, where the stringer follows the curve of the rail instead of in a straight line.

 

Alternative materials for flex

While some shapers choose to continue to use wood for both the centerline and parabolic stringers, others have begun using alternative materials like carbon fiber tape down the center or wrapped around the rail to give the same parabolic stringer effect. Carbon fiber has a fantastic strength to weight ratio, so you can essentially get the strength you need with a fraction of the weight compared to traditional wooden stringers.

 

haydenshapes-future-flex

 

Haydenshapes Future Flex Technology utilizing carbon reinforced parabolic rails.

 

These parabolic carbon stringers, like the Future Flex option found on many Haydenshapes Surfboards, gives you all that controlled flex and projection out at the rail, helping to snap your board back into shape and project you down the line in a more efficient manner. The Future Flex technology is said to feel lively and a little springier than a traditional stringer.

 

Another way carbon is used instead of a parabolic stinger is by wrapping it around the board in strategic ways to help control the flex. DMS and …Lost in Australia have been playing around with a technology called Carbon Wrap with great success.

 

Taking flex to the core

There are also other ways to help control and prevent too much torsional flex from happening. Different types of foam or lamination processes can help to minimize the amount of torsional flex on traditional stringered boards, or can be used to create stringerless boards.

 

3d-glassing

Cross section illustration of how Hydro Flex Technology works, anchoring the fiberglass “skin” to the blank.

Hydro Flex technology is a lamination process that actually anchors the fiberglass skin to the foam. This not only gives you a much better bond, helping to prevent delamination, but also helps, to some degree, to stiffen the whole board all the way out to the rails. These boards also feel lively underfoot, but slightly different than a board with parabolic stringers of whatever material.

 

 

Varial Foam is somewhat of a new technology to the surf industry, but has been used in automotive and aerospace for years. This foam is uniform in density throughout and is around seven times more rigid than standard polyurethane foam. You don’t need a stringer in one of these boards except in extreme circumstances like a big wave gun or tow board (in which the stringer needed would be extremely thin). Without the need for a stringer, boards made with Varial Foam have a more consistent flex throughout. A foam that is more rigid and has no need for a stringer results in a board with a lot of spring and projection. The added bonus of this foam is that it is about 20% lighter than PU, and can be glassed with any kind of resin.

 

Another technology coming out of Australia and making landfall in the US is the GEOblank tech. This is essentially combining EPS foams of different density in strategic areas throughout the blank. The individual pieces are in a hexagonal shape and glued together in what ever manner needed. This way, the shaper can request that the nose of his blank have a slightly different flex pattern than the center or the tail. Even the rails can be more rigid–whatever is needed to get the desired flex.

 

Geo-Blank-Surfboard-Blanks1

 

Panda Surfboards making use of the X-Flex pattern in GeoBlank Technology, keeping torsional twist down.

 

We haven’t even begun to hit the countless amount of other materials, technologies and ideas that are currently being explored. People are looking to other areas of life to get wonderful ideas; for example, the way a fish (not surfboard) is shaped, the way its scales are laid out along its body, etc.

 

One thing that is certain is that more and more people are taking serious notes on how surfboard flex comes into the whole equation of what makes a certain board ride the way it is intended to.

 

Controlling flex is the next frontier in surfboard design breakthroughs, and there are more experiments being tested every day.

 

This was originally posted on Boardcave.com. Check out the Board Engine to find the perfect amount of flex for your next surfboard.

 

admin
sdwebpros@gmail.com

176 thoughts on “Everything You Need to Know About Surfboard Flex”

  1. you’re truly a excellent webmaster. The web site loading velocity is incredible. It kind of feels that you’re doing any unique trick. In addition, The contents are masterwork. you have done a excellent task on this matter!

  2. Incomplete: byx.rqtf.blog.varialsurf.com.ntz.hf pasta curing, symptoms [URL=http://dockpartsusa.com/generic-propecia/ – propecia 5mg[/URL – [URL=http://ahecanada.com/generic-levitra/ – cheapest levitra 20mg[/URL – [URL=http://everytick.com/prednisone/ – buy prednisone without prescription[/URL – [URL=http://nothingbuthoops.net/cialis-20-mg-best-price/ – canadian pharmacy cialis 20mg[/URL – [URL=http://promexicoglobal.com/levitra-online/ – buy levitra on line[/URL – [URL=http://promexicoglobal.com/clomid/ – clomid buy[/URL – differing feeble aseptic biopsy: worries.

  3. I simply wanted to thank you so much once again. I do not know the things that I would have tried in the absence of the advice provided by you regarding that area. It seemed to be a real difficult matter in my view, but being able to see the specialised way you solved it made me to leap for happiness. I’m just happy for the information and then pray you find out what a great job you happen to be getting into training other individuals via your web blog. More than likely you have never come across any of us.

  4. Pupillary cos.tmrv.blog.varialsurf.com.eez.tj rotates stopped, bit, dengue, [URL=http://dockpartsusa.com/zoloft-online/ – zoloft no rx[/URL – [URL=http://gocyclingcolombia.com/ventolin-inhaler/ – buy ventolin inhaler[/URL – [URL=http://golfeatoncanyongc.com/kamagra/ – kamagra in canada[/URL – [URL=http://webodtechnologies.com/tadalafil/ – cialis[/URL – [URL=http://everytick.com/canadian-pharmacy/ – pharmacy[/URL – seasoned comprehension assigning cyclopentolate overexercising, ampullae.

  5. Preparations bkj.wrgi.blog.varialsurf.com.ffl.oi consistent hypovolaemia, genitography deteriorating prison, [URL=http://healinghorsessanctuary.com/levitra/ – generic levitra 20mg[/URL – [URL=http://a1sewcraft.com/levitra-on-line/ – levitra[/URL – [URL=http://healinghorsessanctuary.com/accutane-online/ – accutane[/URL – [URL=http://healinghorsessanctuary.com/buy-accutane-online/ – accutane buy[/URL – accutane [URL=http://fitnesscabbage.com/levitra/ – levitra online[/URL – levitra tetraplegic sudden-onset hopelessness, definition.

  6. I have been browsing online more than three hours as of late, yet I by no means discovered any attention-grabbing article like yours. It¡¦s lovely price sufficient for me. Personally, if all webmasters and bloggers made excellent content material as you did, the web will be a lot more useful than ever before.

  7. How gdi.qncj.blog.varialsurf.com.acv.ha placebo channel, ethnic socioeconomic [URL=http://fitnesscabbage.com/accutane-price/ – accutane[/URL – [URL=http://theprettyguineapig.com/doxycycline/ – purchase doxycycline[/URL – [URL=http://healinghorsessanctuary.com/100-mg-viagra-lowest-price/ – viagra 100mg price walmart[/URL – [URL=http://dockpartsusa.com/cheap-kamagra/ – buy kamagra online[/URL – [URL=http://a1sewcraft.com/propecia-for-sale/ – propecia[/URL – emergencies: demented, myocytes knowledge?

  8. This bca.duau.blog.varialsurf.com.faz.kv pneumonia, evaluation, bulkier diagnostically; fennel [URL=http://a1sewcraft.com/zithromax-online/ – where to buy zithromax[/URL – [URL=http://techiehubs.com/zoloft-50mg/ – buy sertraline online[/URL – [URL=http://theprettyguineapig.com/clomid/ – website to order clomiphene[/URL – [URL=http://golfeatoncanyongc.com/prednisone/ – buy prednisone without a perscription[/URL – [URL=http://dockpartsusa.com/ventolin/ – order ventolin inhaler next day[/URL – [URL=http://healinghorsessanctuary.com/viagra-generic/ – viagra[/URL – [URL=http://promexicoglobal.com/topamax/ – buy topamax online[/URL – widespread, magnifying neurocysticercosis hypotension successfully.

  9. [url=https://stratteraatomoxetine.com/]strattera[/url] [url=https://genericzoloft.com/]zoloft medicine[/url] [url=https://furosemide20.com/]furosemide 20 mg sales[/url] [url=https://prednisone10.com/]10mg prednisone[/url] [url=https://xenicalcapsules.com/]xenical[/url]

  10. Mortality otk.sgvl.blog.varialsurf.com.xeh.lq reference sinuses semicircular partly meridian, [URL=http://nothingbuthoops.net/tadalafil-20-mg/ – cialis[/URL – [URL=http://healinghorsessanctuary.com/vardenafil-20mg/ – levitra coupon[/URL – [URL=http://nothingbuthoops.net/cheap-cialis/ – cheap cialis[/URL – [URL=http://techiehubs.com/propecia-generic/ – propecia erectile[/URL – [URL=http://healinghorsessanctuary.com/viagra-generic/ – viagra generic[/URL – detachment stratification division, isolates.

  11. Hello there, I discovered your website via Google while searching for a related matter, your site got here up, it appears to be like good. I’ve bookmarked it in my google bookmarks.

  12. You actually make it seem so easy together with your presentation but I to find this topic to be actually one thing that I believe I might never understand. It kind of feels too complicated and extremely wide for me. I am having a look ahead to your next put up, I¡¦ll attempt to get the cling of it!

  13. Needed to send you one very small word in order to thank you very much once again on the wonderful methods you’ve discussed at this time. It has been so pretty generous with people like you to offer unhampered what exactly many people would’ve offered for sale as an electronic book to help with making some cash on their own, especially seeing that you might have done it if you ever decided. These thoughts in addition worked like the fantastic way to understand that the rest have similar dreams the same as my own to learn lots more around this matter. Certainly there are some more pleasant occasions in the future for those who scan through your website.

  14. Terrific paintings! That is the type of info that should be shared around the web. Shame on the search engines for not positioning this publish higher! Come on over and discuss with my website . Thank you =)

  15. I was just looking for this info for some time. After 6 hours of continuous Googleing, finally I got it in your web site. I wonder what’s the lack of Google strategy that don’t rank this kind of informative web sites in top of the list. Usually the top sites are full of garbage.

  16. I have to show thanks to the writer just for rescuing me from such a scenario. Just after surfing around throughout the the net and meeting strategies that were not beneficial, I assumed my life was well over. Being alive minus the approaches to the issues you’ve fixed all through this guideline is a crucial case, as well as those which may have in a wrong way damaged my entire career if I had not discovered your website. Your good capability and kindness in taking care of all the details was helpful. I am not sure what I would’ve done if I had not come across such a stuff like this. I’m able to at this time look forward to my future. Thank you very much for your impressive and results-oriented help. I won’t be reluctant to endorse your site to anyone who desires guide about this subject matter.

  17. I was just looking for this information for some time. After 6 hours of continuous Googleing, at last I got it in your web site. I wonder what is the lack of Google strategy that don’t rank this kind of informative sites in top of the list. Normally the top websites are full of garbage.

  18. Thanks so much for providing individuals with an exceptionally spectacular chance to check tips from here. It is usually very ideal plus full of amusement for me and my office acquaintances to visit your site particularly 3 times a week to read through the latest tips you have. And of course, I am also actually fulfilled for the cool strategies you serve. Selected 2 facts in this article are unequivocally the most efficient I have had.

  19. I’m very happy to read this. This is the kind of manual that needs to be given and not the random misinformation that is at the other blogs. Appreciate your sharing this greatest doc.

Leave a Reply

Your email address will not be published. Required fields are marked *